Methods and compositions for repair of cartilage using an in vivo bioreactor

ABSTRACT

Methods and compositions for the biological repair of cartilage using a hybrid construct combining both an inert structure and living core are described. The inert structure is intended to act not only as a delivery system to feed and grow a living core component, but also as an inducer of cell differentiation. The inert structure comprises concentric internal and external and inflatable/expandable balloon-like bio-polymers. The living core comprises the cell-matrix construct comprised of HDFs, for example, seeded in a scaffold. The method comprises surgically removing a damaged cartilage from a patient and inserting the hybrid construct into the cavity generated after the foregoing surgical intervention. The balloons of the inert structure are successively inflated within the target area, such as a joint, for example. Also disclosed herein are methods for growing and differentiating human fibroblasts into chondrocyte-like cells via mechanical strain.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims priority to U.S. Provisional ApplicationSer. No. 60/771,172, entitled Method for Repairing an IntervertebralDisc, and filed on Feb. 7, 2006 and also claims priority to U.S.Provisional Application Ser. No. 60/785,478, entitled Multi-LayeredMulti-Compartmental Three-Dimensional Polymeric Scaffold ForIntervertebral Disc Repair, and filed on Mar. 24, 2006, both of whichare incorporated by reference herein in their entirety.

FIELD OF THE INVENTION

The present invention generally concerns at least the fields ofmedicine, surgery, anatomy, biology, cell biology, and/or molecularbiology. In particular aspects, the present invention concerns thefields of cartilage repair, such as articular cartilage repair. Moreparticularly, the field of the invention concerns cell-matrixencapsulation devices for growing, proliferating, and/or differentiatingcells into chondrocyte-like cells under mechanical stress.

BACKGROUND OF THE INVENTION

Typically, articular cartilage is a tissue that is not naturallyregenerated once damaged. Recently, efforts have been made toreconstruct damaged biological tissues by regenerating a portion of thedamaged tissues in laboratories. This approach, defined as “tissueengineering” has raised tremendous attention.

Tissue engineering involves the development of biocompatible materialscapable of specifically interacting with biological tissues to producefunctional tissue equivalents. Tissue engineering has a basic concept ofcollecting a desired tissue from a patient, isolating cells from thetissue specimen, proliferating cells, seeding the proliferated cellsonto a biodegradable polymeric scaffold, culturing the cells for apredetermined period in vitro, and transplanting back the cell/polymerconstruct into the patient. After transplantation, the cells in thetransplanted scaffold use oxygen and nutrients gained by diffusion ofbody fluids to proliferate and differentiate to form a new tissue,whereas the scaffold has been dissolved.

The scaffold used for the regeneration of biological tissue is usuallycomprised of a material that serves as matrix to allow cells to attachto the surface of the material and form a three dimensional tissue. Thismaterial should be non-toxic, biocompatible and biodegradable. The mostwidely used biodegradable polymers, satisfying the aforementionedphysical requirements, include organic polymers such as polyglycolicacid (PGA), polylactic-co-glycolic acid (PLGA), poly-E-caprolactone(PCL), polyamino acids, polyanhydrides, polyorthoesters; naturalhydrogels such as collagen, hyaluronic acid, alginate, agarose,chitosan; synthetic hydrogels such as poly(ethylene oxide) (PEO),poly(vinyl alcohol) (PVA), poly(acrylic acid) (PAA), poly(propylenefumarate-co-ethylene glycol) [P(PF-co-EG) and copolymers thereof.

The aforementioned polymers have been researched to fabricate porousscaffold. However, conventional fabrication techniques generally resultin scaffolds with low porosities that do not adequately support cellgrowth. The pores on the surface of the scaffold are often blocked,nutrients are not sufficiently supplied to the cells, and cells havedifficulties in growing into the scaffold. Recently, the application ofmicro-fabrication technology in the field of tissue engineering hasrendered possible the development of complex scaffold with micron-scaleresolution. These scaffolds referred to as “microfluidic scaffolds”present a network of micro-channels that allow fluid flow within thescaffold. This network of micro-channels helps to provide both nutrientsand soluble factors to distinct sections of the scaffold.

The scaffold can also be encapsulated with a semi-permeable membrane.U.S. Patent Publication No. 2006/0147486 relates to a porous scaffoldenveloped with a semi-permeable membrane. This semi-permeable membraneselectively introduces nutrients into the scaffold from outside thescaffold, as well excreting metabolic wastes generated by the tissuecells to the outside of the scaffold. The publication describes themethod to grow cells within this scaffold in vitro for regenerating abiological tissue.

U.S. Pat. No. 6,627,422 describes a device containing cells in a yarnmatrix encapsulated in a semi-permeable membrane. In this case, thesemi-permeable membrane allows implanted cells to receive nutrients butalso allows therapeutic molecules produced by the implanted cells todiffuse to host cells. This device is used for cell therapy: theencapsulated cells secrete endogenous proteins to the host. This devicefunctions as a bioartificial organ (for example, as artificial pancreasby secreting insulin).

Despite such progress in the engineering of scaffolds with improveddiffusion of nutrients, the scaffold once transplanted to the patientsuffers from a limited supply of nutrients. Indeed, in vivo, nutrientsand oxygen are delivered to disc cells through blood vessels in theendplates of the vertebrae adjacent to the disc. In degenerative discdisease, the vertebral endplates of vertebrae are not well-functioningand do not allow sufficient diffusion of nutrition to the implantedcell-scaffold.

Different cell types can be used to engineer articular cartilage.Primary differentiated cells of articular cartilage (i.e. chondrocytes)from biopsies of existing cartilage can be used. These cells are oftenprocured from an autologous source since the procurement of heterologouscells or cells from cadavers carries the inherent risk of transfer ofpathogens. Mesenchymal Stem Cells (MSCs), which are embryonic-like cellsfound in bone marrow, are capable of differentiation into different typeof mesenchymal tissues and especially cartilaginous tissue; therefore,they are another cell source for cartilage engineering.

However, these cell sourcings raise many issues. Chondrocytes fromintervertebral disc are difficult to harvest, because the autologouscells are obtained from the patient's disc and therefore it requires aninvasive procedure (back surgery) to perform a biopsy. If cells areharvested from a healthy disc, it jeopardizes the functioning of thehealthy disc. If cells are harvested from a damaged disc during thediscectomy, it provides abnormal cells from a degenerated tissue.Moreover, chondrocytes are difficult to expand in culture since theyde-differentiate. Regarding chondrocytes from other cartilages, theelastic cartilage from the ear is easy to harvest, but it produces onlyhyaline cartilage and not fibro-cartilage, as in the disc. MSCs alsohave some disadvantages, because they require a bone marrow biopsy.While a large quantity of cells is needed for tissue engineering, it isdifficult to obtain a large quantity of adult stem cells.

Numerous papers have reported the culture conditions that stimulatechondrogenesis of mesenchymal stem cells or de-differentiatechondrocytes. These conditions are the following: high density micromassculture; hypoxia; supplementation with growth factors, such as BoneMorphogenetic Proteins (BMP) particularly BMP-2, -4, -6, and -7,transforming growth factor beta (TGF-β), and/or insulin growth factorone (IGF-I); supplementation with ascorbic acid; culture on specificmatrix, such as alginate; culture under mechanical stress such asIntermittent Hydrostatic Pressure (IHP) (Watt, 1988; Dozin et al., 1992;Sullivan et al., 1994; Denker et al., 1999; Zur Nieden et al., 2005;Zhou et al., 2004; Majumdar et al., 2001; Barry et al, 2001; Elder etal., 2005; Mow et al., 1992; Domm et al., 2000).

Few studies have reported the conversion of Human Dermal Fibroblasts(HDFs) into chondrocyte-like cells. U.S. Pat. No. 6,489,165 concerns theconversion of HDFs into chondrocyte-like cells under high densitymicromass culture and hypoxia. French MM et al. (2004) reported theconversion of HDFs into chondrocyte when the cells are grown on theproteoglycan, aggrecan, and supplemented with insulin growth factor one(IGF-I).

Degenerative Disc Disease

Degenerative Disc Disease (DDD) requires 700,000 procedures each yearperformed by 4,500 spine surgeons, and the majority of disc disordersoccur in young patients. Therefore, it is critical to develop effectiveand safe strategies to treat this disease.

An intervertebral disc (IVD) is a complex structure comprising threedistinctive tissues: the annulus, the nucleus, and cartilage endplates.The annulus is a well-organized, multi-layered structure of collagenfibers. The nucleus is comprised mainly of glycosaminoglycan(hydrophilic polymer). The cartilage endplates supply nutrients. Theforegoing combination allows the normal disc to perform two conflictingfunctions: stability and flexibility.

The intervertebral disc absorbs shocks, maintains motion, and keepsstability. Similar to other cartilages, the innate repair capacity ofthe intervertebral disc (which acts as a joint between two vertebra) islow, because it is avascular and nutritionally supported only by passivediffusion at the endplates. Consequently, once the degenerative processis activated, it is ultimately considered to be an irreversiblecondition. Once damaged, the degenerated disc may bulge or extrude, andtherefore needs to be removed.

Currently, the common surgical treatment for patients with chronic lowback pain due to degenerative disc disease is either discectomy orspinal fusion. Discectomy is an appropriate procedure and is routinelyperformed to remove the degenerated nucleus through a fenestrationwithin the annulus: it allows removal of both the extruded nucleus(herniectomy) and the degenerated remaining inter-vertebral nucleusfragments. Although this procedure is ideal for decompressing andrelieving the nervous system (root or cauda equina), it is a pooroperation for the spine, because it creates a potentially disablingcondition that leads to a degenerative cascade that may require anadditional invasive surgical procedure, like fusion or arthroplasty, forexample. Discectomy brings a good short-term effect in relievingradicular pain, but it causes disc height reduction with neuro-foramenstenosis, instability of the treated level, poor result on back pain,and/or complications, such as spinal stenosis or facet pain, forexample.

Spinal fusion is the most effective treatment for low back pain. It is asurgical procedure in which an entire disc is removed and the twoadjacent vertebrae are united together (“fused”) with the interpositionof a graft (cages, bone grafts, and/or fixation devices, for example).It is indicated for patients with advanced disc degeneration. Over200,000 spinal fusions are performed each year in the U.S. alone, but byeliminating the motion, the spinal fusion alters the biomechanicalproperties of the inter-vertebral disc and increases stress and strainon the discs that are adjacent to the fused disc. In fact, bothdiscectomy and fusion worsen the condition of the affected disc,adjacent discs, and surrounding tissues (such as facet joints), leadingto further degeneration.

The failure of these procedures has led to a search for the developmentof non-fusion technologies, such as disc or disc nucleus prosthesis, forexample. Disc arthroplasty with an artificial disc is an emergingtreatment for patients with disc degeneration. Its advantages are tomaintain motion, decrease incidence of adjacent segment degeneration,avoid complications related to fusion, and allow early return tofunction. Today, two kinds of devices are marketed: the total discreplacement and the nuclear replacement, but both of them have majorpitfalls. Total disc replacement is a bulky metallic prosthesis designedto replace the entire disc: annulus, nucleus and endplates. Theseprostheses use an invasive anterior (trans- or retro-peritoneal)approach that requires the presence of a vascular surgeon.Dislodgements, wear debris, degeneration of adjacent intervertebraldiscs, facet joint arthrosis, and subsidence of this type of prosthesishave been reported. The artificial nucleus substitute preserves theremaining disc tissues and their functions. Its design allows itsimplantation through a posterior approach, but the major limitation ofsuch nucleus prosthesis is that it can be used only in patients in whomdisc degeneration is at an early or intermediate stage, because itrequires the presence of a competent natural annulus. Implant extrusionremains a primary concern. As a hydrogel-based device, it is fragile,and so does not resist the outstanding bio-mechanical constraints of thelumbar spine (shear forces). As inert materials, they may lose theirmechanical properties over time, and tears and breakages have beenreported. Replacing the nucleus only and leaving in place a damagedannulus generates the conditions for implant extrusion or recidivism ofdiscal herniation.

Tissue engineering and regenerative medicine represent a new option forthe treatment of DDD. A variety of approaches are used to regeneratetissues. These approaches can be categorized into three groups: 1)biomaterials, without additional cells, that are used to send signals toattract cells and promote regeneration; 2) cells alone may be used, toform a tissue; and 3) cells may be used with a biomaterial scaffold thatacts as a frame for developing tissues. While Autologous ChondrocyteTransplantation (ACT) has been used for a few years to repair articularcartilage, tissue engineering for disc repair remains in its infancy.Intensive research is currently done, and animal studies have shown thefeasibility of tissue-engineered intervertebral disc. Moreinterestingly, recent pilot clinical studies have shown that ACT is anefficient treatment of herniated disc. The main disadvantage of ACT fordisc repair is that it requires a disc biopsy. Therefore, there is aneed for an improved method to restore disc anatomy and improve itsfunctioning, and there thus remains a need for an improved method ofcartilage repair. The present invention seeks to meet these and otherobjects and provides a solution to a long-felt need in the art.

SUMMARY OF THE INVENTION

The present invention concerns methods and compositions for biologicalrepair of any kind of cartilage, including intervertebral and jointcartilage, for example. More specifically, but not exclusively, thepresent invention relates to methods and compositions for biologicalrepair of cartilage using an implantable device that is a combination ofan inert structure acting as an in vivo bioreactor, and a livingstructure comprised of chondrocytes or chondrocyte-like cells, forexample, such as cells derived from the exemplary Human DermalFibroblasts (HDFs), in specific embodiments. More particularly, but notexclusively, the present invention relates to a hybrid constructcombining both an inert structure and living core. The inert structureacts not only as a delivery system to feed and grow a living corecomponent, but also acts as an inducer of cell differentiation, incertain aspects. In embodiments of the invention, this inert structurecomprises two expandable balloon-like bio-polymers, namely, an internalmembrane (like a balloon) that is enclosed within an external membrane(also like a balloon). Hence, the inert structure comprises twogenerally concentric inflatable membranes. The two membranes may befurther defined as a first enclosed membrane that is structurally withina second enclosed membrane. In specific embodiments, the shapes may beconsidered to be generally spherical, generally elliptical, generallyrounded, generally orbed, generally discoid, generally spheroidical,generally globule, balloon-like, and so forth. In additional specificembodiments, the shape is individual-specific and conforms to the shapeand size of the remaining cavity in the joint or intervertebral discregion of the individual.

In certain aspects, the invention generates natural tissue in vitro,such as from stem cells, chondrocytes, and so forth. More particularly,but not exclusively, the present invention relates to a method forgrowing and differentiating Human Fibroblasts into chondrocyte-likecells, for example. The cells, which are autologous in certainembodiments, are put into a scaffold matrix made of one or morebiopolymers, such as to mimic a natural matrix. The scaffold may beseeded in vitro, and in certain aspects growth factors are provided tothe cells, the matrix, or both. The scaffold is put into a bioreactor,which is a system for perfusion of medium and allows application ofmechanical force to the scaffold. Following delivery of the force, cellsare assisted in differentiation, especially for generation of cartilage.

In specific embodiments, the invention employs differentiation ofcertain cells into chondrocyte-like cells. In specific embodiments,HDFs, for example, are differentiated into chondrocyte-like cells underparticular culture conditions, such as hypoxia (Nicoll et al., 2001),high density micromass culture, and culture on specific matrix, such asaggrecan (French et al., 2004). In specific embodiments, factors thatmimic the in vivo environment of intervertebral chondrocytes are potentstimuli for chondrogenic differentiation of HDFs, for example; suchfactors include the following: 1) three dimensionality; 2) low oxygentension (<5%); and 3) mechanical stress; and 4) intermittent hydrostaticpressure. In specific embodiments, cell viability and chondrogenicdifferentiation of HDFs seeded in three-dimensional alginate beadcultures are determined. In another embodiment, the effects of oxygentension on the differentiation of HDFs cultured in alginate beads arecharacterized. In an additional specific embodiment, the effects ofhydrostatic compression on the differentiation of HDFs cultured inalginate beads are characterized.

Differentiation of cells into chondrocytes or chondrocyte-like cells mayoccur in any suitable manner, including differentiation in vitro priorto implantation of the device into an individual or differentiation invitro prior to implantation of the device into an individual and also invivo following implantation.

In specific embodiments the device of the invention provides a methodfor in vivo regeneration of a joint, such as an intervertebral disc,elbow, knee, shoulder, hip, temporo-mandibular joint, and so forth. Incertain aspects of the invention, a living compartment comprises thecell-matrix construct of chondrocyte-like cells, such as are derivedfrom HDFs, seeded in a biomaterial. The culture and differentiation ofthe living compartment may be initiated in vitro, in certainembodiments. The living core is seeded in the inert biomaterial andimplanted, and the cells continue to proliferate and differentiate invivo.

In certain embodiments, the cartilage that is the focus of applicationof the invention is intervertebral disc cartilage. In particular aspectsof the invention, cells utilized in the invention are subjected tomechanical strain for chondrogenic differentiation. Thus, embodiments ofthe invention provide an inter-vertebral inert structure acting as an invivo bioreactor for inducing growth and differentiation of a livingcore. In further embodiments, the invention provides a hybrid constructcombining both an inert structure and living core for implantation intothe inter-somatic space using a minimally invasive surgery.

It is an exemplary object of the present invention to provide a methodintended to repair a degenerated intervertebral disc, e.g. restoreintervertebral disc anatomy and improve its functioning. In particularaspects of the invention, there is provided a method to repair damageddisc using a hybrid structure made of an inert containing deviceintended to feed and differentiate an inner living core. Therefore, theinert structure acts as a delivery system of nutrients and growthfactors and as a bioreactor able to differentiate autologous dermalfibroblasts into chondrocyte-like cells. Under mechanical stress (suchas intermittent hydrostatic pressure, and/or fluid shear stress), thecells will acquire the characteristics of nucleus cells in the centralpart and annulus cells in the periphery. Exemplary fibroblast-derivedchondrocyte-like cells may be harvested from skin, such as by a biopsy,and then seeded onto three-dimensional polymer scaffold for use of therepair of the disc. This would obviate the need for invasive techniqueto harvest autologous chondrocytes, in particular aspects. An advantageof certain aspects of the inventive hybrid construct that combines bothan inert biomaterial acting as a nutrient-delivery system and livingcells easily harvested from skin, for example, is that it is capable ofself-maintenance or remodeling and may restore the disc function using aminimally invasive posterior surgical approach, for example.

In certain aspects of the invention, the damaged cartilage from thejoint or intervertebral space is removed and the hybrid structure isinstalled within the space provided by the foregoing removal. In someembodiments of the invention, the device is implanted using a minimallyinvasive surgical procedure. In specific embodiments, an exemplarysurgical technique is employed. In general embodiments forintervertebral discs, when an intervertebral disc must be removed frombetween two adjacent vertebrae, e.g. in the lumbar spine, it is lessinvasive to surgically proceed posteriorly from the back of the patient.This minimally invasive procedure allows proceeding with the curettageof the inter-somatic space through a small aperture within the annulus(annulotomy) for removing the degenerated fragments of the disc'snucleus. Using this small annulus opening, the present invention employsa novel intervertebral repairing pack that can be slid through theaforementioned incision and then expanded into the area generated by thenucleus removal within the inter-somatic space, for example. In specificembodiments, the removal of the damaged disc and the installation of thetissue-engineered construct are done in the same posterior operation,thereby minimizing risks, chances of surgical complications andre-interventions, as well as surgery time.

In one embodiment of the invention, there is an implantable devicecomprising a cells/scaffold composition and an encapsulating device,wherein the encapsulating device comprises a first generally concentricmembrane; a second generally concentric membrane that is concentricallyexternal to the first generally concentric membrane; a first volumewithin the first generally concentric membrane; a second volume that isexternal to the first generally concentric membrane and that is internalto the second generally concentric membrane; and a structure forextracting material from the second volume, wherein the first generallyconcentric membrane is semi-permeable and houses the cell/scaffoldcomposition. A membrane may be considered generally concentric comparedto another if the centers of each of the membrane are substantiallynearby.

In certain aspects of the invention, an individual is provided anothertherapy in addition to the implantable device of the invention. Forexample, before, during, and/or after implantation of the device, theindividual may receive one or more antibiotics. Exemplary post-operativetherapies includes Non Steroidal Anti-Inflammatory Drugs (NSAIDs),simple pain killers (analgesics), and/or myo-relaxing medication asneeded, and it may be followed by a functional rehabilitationpost-operatively, such as after the first, second, third or morepost-operative week, for example.

In some embodiments, there is a hybrid structure for cartilage repaircomprising an encapsulating device comprised of inert material and aliving core comprised of chondrocyte-like cells. This encapsulatingdevice acts as an in vivo bioreactor for cartilage engineering. Itallows in vivo growth and differentiation of cartilage cells byproviding growth factors and nutrients and transmitting a physiologicloading regimen.

In one embodiment of the invention, there is an implantable device,comprising a cells/scaffold composition; and an encapsulating devicethat comprises: a first membrane having an inside and an outside; asecond membrane having an inside and an outside, wherein the firstmembrane is encapsulated inside the second membrane; a first volumedisposed inside the first membrane; a second volume that is disposedoutside the first membrane and that is disposed inside the secondmembrane; and a structure for adding fluid to the second volume,removing fluid from the second volume, or both, wherein thecells/scaffold composition is disposed inside the first membrane and thefirst membrane has one or more of the following characteristics:semi-permeable; biocompatible; biodegradable; and resorbable, whereinthe second membrane has one or more of the following characteristics:biocompatible; hermetic to fluid; permeable to oxygen; resorbable;biodegradable; and expandable.

In a specific embodiment, the scaffold is comprised of a syntheticpolymer, a natural hydrogel, or a synthetic hydrogel. In an additionalspecific embodiment, the synthetic polymer is polyglycolic acid,polylactic acid, polylactic-co-glycolic acid, poly-ε-caprolactone, orpoly(glycerol-Sebacate) (PGS). In another specific embodiment, thesynthetic polymer is a polyphosphazene, a polyanhydride, or apoly(orthoester). In particular embodiments, the natural hydrogelcomprises collagen, hyaluronic acid, alginate, agarose, chitosan,fibrin, gelatin, or a copolymer thereof. In a further embodiment, thesynthetic hydrogel comprises poly(ethylene oxide), poly(vinyl alcohol),poly(acrylic acid), poly(propylene fumarate-co-ethylene glycol), or acopolymer thereof.

In certain aspects of the invention, the cells in the device arechondrocyte cells or chondrocyte-like cells, such as wherein thechondrocyte cells or chondrocyte-like cells secrete a molecule selectedfrom the group consisting of aggrecan, type II collagen, Sox-9 protein,cartilage link protein, and perlecan. In particular cases, the cellswere differentiated from fibroblast cells and/or stem cells. Exemplaryfibroblast cells are dermal fibroblasts, tendon fibroblasts, ligamentfibroblasts, synovial fibroblasts, foreskin fibroblasts, or a mixturethereof.

In particular aspects, the first membrane is comprised of abiodegradable, biocompatible, and resorbable polymer. In furtheraspects, the first membrane is comprised of a polyacrylate, apolyvinylidene, a polyvinyl chloride copolymer, a polyurethane, apolystyrene, a polyamide, a cellulose acetate, a cellulose nitrate, apolysulfone, a polyphosphazene, a polyacrylonitrile, apoly(acrylonitrile/covinyl chloride) or a derivative, copolymer ormixture thereof. In specific aspects, the first membrane is generated bypolyelectrolyte complexation. In specific aspects, the second membraneis comprised of polyglycolic acid (PGA), polylactic acid (PLA),polylactic-co-glycolic acid (PLGA), poly-ε-caprolactone (PCL),polyurethane (PU), polydioxanone (PDO), a polyethylene, poly (glycerolsebacate) (PGS), or a derivative, copolymer, or mixture thereof. Inadditional embodiments, the rate of resorbability of the second membraneis slower than the rate of resorbability of the first membrane.

In particular embodiments, the implantable device comprises one or morenutrients, growth factors, and/or medicaments. In some cases, theimplantable device may be further defined as comprising a basal cellculture medium comprising the one or more nutrients, growth factors,and/or medicaments. In specific embodiments, the medium is supplementedwith Fetal Bovine Serum (FBS), ascorbic acid, and/or dexamethasone. Thenutrients, growth factors, and/or medicaments may be present in thescaffold, the first volume, the second volume, or a combination thereof,in certain cases. The growth factor is selected from the groupconsisting of bone morphogenetic protein 2 (BMP-2), BMP-4, BMP-6, BMP-7,cartilage-derived morphogenetic protein (CDMP), transforming growthfactor beta (TGF-β), insulin growth factor one (IGF-I), fibroblastgrowth factors (FGFs), basic fibroblast growth factor (bFGF), FGF-2,platelet-derived growth factor (PDGF), and a mixture thereof, inspecific embodiments, and the medicament may be further defined as oneor more of an antibiotic, antifungal agent, or antiviral agent.

In certain aspects of the invention, the structure comprises one or moretubes and/or comprises one or more catheters and/or one or morereservoirs. In particular cases, the structure is further defined ascomprising one or more of a first tube; a second tube; optionally, afirst reservoir; and optionally, a second reservoir. In a specificembodiment, the first and second tubes respectively comprise first endspositioned within the second volume, wherein the first and second tubesrespectively comprise second ends connected to first and secondreservoirs, or both. The first and/or second tubes are comprised of thesame material as the second membrane, in one exemplary case, and thefirst and/or second tubes are comprised of silicone rubber, in oneexemplary case.

In one embodiment of the invention, there is a method of repairingdamaged cartilage in a joint (such as an intervertebral disc) of anindividual, comprising delivering a device in accordance with theinvention to the respective joint (such as intervertebral disc) of theindividual. In a specific aspect, the method further comprises preparingthe cells/scaffold composition under suitable ex vivo conditions. Inanother specific embodiment, preparing the cells/scaffold composition isdefined as subjecting one or more cells to a scaffold under suitableconditions. Preparing of the cells/scaffold composition may occur for noless than about two to three days, in certain aspects of the invention.In a specific embodiment, the suitable conditions allow proliferation ofthe cells, such as, for example, allowing the stimulation ofchondrogenic differentiation. Suitable conditions may be further definedas being under high density micromass culture, being under low oxygentension (between about 1.0%-7.5%), being under mechanical stress, and/orbeing fed by a medium supplemented with growth factors, ascorbic acid,and/or dexamethasone, in exemplary embodiments.

In particular embodiments, the cells/scaffold composition is subjectedto mechanical stress, which may be hydrostatic pressure, fluid shearstress, or a combination thereof, for example. In a specific embodiment,the mechanical stress is intermittent. In particular cases, themechanical stress is fluid shear stress and the scaffold is microfluidicscaffold.

In other particular embodiments, the delivering step is defined asimplanting the device using minimally invasive surgery. In one exemplarycase, following implantation of the device into the individual, thesecond membrane is inflated to fill a void in the joint, such as anintervertebral disc. In another exemplary case, prior to delivery of thedevice to an intervertebral disc of the individual, at least part of anendogenous intervertebral disc was removed from the individual. Thejoint of concern with the invention may be an intervertebral disc, aknee, a shoulder, an elbow, a hip, or a temporo-mandibular joint, inspecific embodiments.

In certain aspects of the invention, the structure of the devicecomprises: a first tube having first and second ends, said first end ofthe first tube disposed within the second volume; a second tube havingfirst and second ends, said first end of the second tube disposed withinthe second volume; a first reservoir; and a second reservoir, whereinfollowing delivery of the device to an intervertebral disc in theindividual and following inflation of the second membrane, the secondends of the first and second tubes are respectively connected to thefirst and second reservoirs. In a specific embodiment, the first andsecond reservoirs are subcutaneously positioned in the individual.Methods of the invention may further comprise sealing the firstmembrane, sealing the second membrane, or both. In a specific aspect, atleast part of the second volume is exchanged. In one exemplaryembodiment, the method of the invention further comprises removing atleast part of the second volume through the first reservoir. In anotherspecific aspect, the method comprising removing fluid from the first orsecond reservoir, delivering a fluid to the respective second or firstreservoir, or concomitantly removing fluid from the first or secondreservoir and delivering a fluid to the respective second or firstreservoir.

In certain cases, the cells/scaffold composition is inserted into thefirst membrane prior to delivery of the device into the individual orwherein the cells/scaffold composition is inserted into the firstmembrane subsequent to delivery of the device into the individual. In aspecific embodiment, the first membrane is inserted into the secondmembrane prior to delivery of the device into the individual or whereinthe first membrane is inserted into the second membrane subsequent todelivery of the device into the individual.

In one embodiment of the invention, there is a method of preparing acells/scaffold composition, wherein the cells are chondrocytes orchondrocyte-like cells, comprising: subjecting cells capable ofdifferentiating into a chondrocyte-like cell to the scaffold; subjectingthe cells to mechanical stress; and optionally subjecting the cells toone or more growth factors suitable for differentiation to a chondrocyteor chondrocyte-like cell. In a specific embodiment, the mechanicalstress is intermittent.

In a further embodiment, there is a kit comprising the device of theinvention, wherein the device is housed in one or more suitablecontainers. In specific embodiments, the kit further comprises cellsthat are chondrocyte cells, chondrocyte-like cells, or cells that arecapable of differentiating to chondrocyte cells or chondrocyte-likecells.

In an additional embodiment, there is an implantable device, comprising:a cells/scaffold composition encapsulated inside a membrane, saidmembrane having an inside and an outside; and a structure for exchangingat least part of fluid that is inside the membrane, wherein the membranehas one or more of the following characteristics: semi-permeable;biocompatible; biodegradable; and resorbable.

In another embodiment, there is a hybrid structure for cartilage repair,comprising: an encapsulating device comprising inert material; and aliving core comprising chondrocyte-like cells, wherein saidencapsulating device encapsulates the living core.

In an additional embodiment, there is an in vivo bioreactor forcartilage engineering, comprising a device that encapsulates cells,wherein said cells are capable of differentiating to chondrocytes orchondrocyte-like cells, wherein the encapsulation of said cells providessuitable conditions for in vivo growth and differentiation of saidcells, wherein said conditions comprise providing a physiologic loadingregimen on said cells. In a specific embodiment, the physiologic loadingregimen comprises force from a spine of an individual.

The foregoing has outlined rather broadly the features and technicaladvantages of the present invention in order that the detaileddescription of the invention that follows may be better understood.Additional features and advantages of the invention will be describedhereinafter which form the subject of the claims of the invention. Itshould be appreciated by those skilled in the art that the conceptionand specific embodiment disclosed may be readily utilized as a basis formodifying or designing other structures for carrying out the samepurposes of the present invention. It should also be realized by thoseskilled in the art that such equivalent constructions do not depart fromthe spirit and scope of the invention as set forth in the appendedclaims. The novel features which are believed to be characteristic ofthe invention, both as to its organization and method of operation,together with further objects and advantages will be better understoodfrom the following description when considered in connection with theaccompanying figures. It is to be expressly understood, however, thateach of the figures is provided for the purpose of illustration anddescription only and is not intended as a definition of the limits ofthe present invention. The present application refers to a number ofreferences and documents all of which are incorporated herein in theirentirety.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present invention, reference isnow made to the following descriptions taken in conjunction with theaccompanying drawings.

FIG. 1 illustrates a cross-section of the exemplary L4-L5 intervertebralspace.

FIG. 2 shows a posterior approach to an intervertebral space, includingexemplary herniated tissue and degenerated discal tissue.

FIG. 3 illustrates an exemplary embodiment of the annulus defectlocation for disc removal.

FIG. 4 shows abdominal cross-section and draining system in embodimentsof the invention, including an exemplary medline incision and exemplaryHolter-Rickham reservoirs (Codman & Shurtleff, Inc.; Raynham, Mass.)

DETAILED DESCRIPTION OF THE INVENTION

As used herein the specification, “a” or “an” may mean one or more. Asused herein in the claim(s), when used in conjunction with the word“comprising”, the words “a” or “an” may mean one or more than one. Asused herein “another” may mean at least a second or more. In specificembodiments, aspects of the invention may “consist essentially of” or“consist of” one or more sequences of the invention, for example. Someembodiments of the invention may consist of or consist essentially ofone or more elements, method steps, and/or methods of the invention. Itis contemplated that any method or composition described herein can beimplemented with respect to any other method or composition describedherein.

I. Definitions

The term “bioreactor” as used herein refers to a system in which abiological conversion is effected. Cells are cultivated in a controlledmanner and are converted via specific reactions, in specificembodiments. In some aspects of the invention, a bioreactor is capableof regulating one or more of the following parameters: temperature,medium pH, exchanges of gases, mechanical stimuli, pO₂, PCO₂, andhumidity. A perfusion system is present in the bioreactor(perfusion-bioreactor), in specific embodiments, to provide constantsupply of nutrients and to remove efficiently the waste products.Mechanical stresses are an important factor of chondrocyte function.Combinations of mechanical stresses are simultaneously developed duringjoint motion on an intermittent basis that includes cell and tissuedeformation, compressive and shear forces, fluid flow, and changes inhydrostatic pressure, for example. These conditions are reproduced withthe bioreactor, in certain aspects.

The term “catheter” as used herein refers to a hollow tube, which may beflexible or rigid, that is employed to drain fluid from an area in thebody.

The term “chondrocyte-like cells” as used herein refers to cells thatare not primary chondrocytes but are derived from stem cells (such asmesenchymal stem cells) or cells from other lineages (such asfibroblasts). These chondrocyte-like cells have a phenotype ofchondrocytes (cells of cartilage). This means that not only do they havea shape of chondrocytes (polygonal and/or rhomboidal cells, forexample), but also they are able to aggregate and produce cartilagematrix components, such as sulfated proteoglycan and type II collagen,for example. Thus, exemplary markers of chondrocyte-like cells includeone or more of aggrecan, which is a chondroitin sulfate and keratansulfate proteoglycan, type II collagen, Sox-9 protein, cartilage linkprotein, and perlecan, which is a heparan sulfate proteoglycan, forexample.

The term “copolymer” as used herein refers to a polymer comprising twoor more different monomers (polymer: a naturally occurring or syntheticcompound comprising large molecules made up of a linked series ofrepeated simple monomers).

The term “de-differentiation” as used herein refers to regression of aspecialized cell or tissue to a simpler, more embryonic, unspecializedform. When chondrocytes are grown ex vivo in monolayers, they lack theirin vivo environment (and especially the three dimensionality andmechanical stress) and undergo morphological and molecular changescalled de-differentiation. This process involves a change in morphologyand a change from expression of chondrocyte-specific genes to that ofgenes that are normally expressed in fibroblasts.

The term “discectomy” as used herein refers to a procedure to removepart or all of a degenerated nucleus through a fenestration within theannulus. It is performed through a minimally invasive approach using anoperative microscope. The procedure frees the roots by removing thecompressive herniated (extruded) nucleus. It allows removing thedegenerated remaining nucleus through a tenotomy (aperture) within theannulus. In particular, a discectomy is actually a herniectomy with theremoval of the degenerated nucleus fragments.

The term “encapsulate” or “encapsulating” as used herein refers toenclosing within a boundary, such as in a membranous sac.

The term “fluid shear stress” refers to the motion of fluids upon asurface, which results in the generation of shear stress. Shear stressis a stress state where the stress is parallel to a surface.Microfluidic scaffold allows fluid flow in the microchannels. This fluidflow induces fluid shear stress on the cells seeding in the scaffold.

The term “hermetic” as used herein refers to being made liquid-tight,such as by fusion or sealing, for example. In particular, a hermeticmembrane does not allow liquid inside it to exit the membrane, althoughit allows oxygen and carbon dioxide to cross the membrane (such asoxygen to enter the membrane and carbon dioxide to leave the membrane).

The term “hydrostatic pressure” refers to the pressure exerted ortransmitted by liquid (for example, water) at rest. The intervertebraldisc is exposed to wide ranges of intradiscal hydrostatic pressureduring different loading exercises and are at their minimum (about 0.25MPa) during lying or relaxed sitting and at maximum (about 2.5 to 5 MPa)during lifting weights with a round back. These different loadingmagnitudes influence the intervertebral disc by alteration of discmatrix turnover depending on their magnitudes. Numerous studies havebeen done to determine the best regimen for intermittent hydrostaticpressure (IHP) to be applied in vitro to the cells to inducechondrogenic differentiation of cells in vitro. Different regimens havebeen tested. In these studies, IHP applied is within the amplituderanges from 0.5 MPa to about 5 MPa and a frequency range from 0.01 Hz to1 Hz. The encapsulating device is designed to transmit in vivohydrostatic pressure to the cell-matrix construct, in specificembodiments. The external envelop filled with liquid (medium) iscompressed during different loading exercises; under this compressionsome liquid medium diffuses through the semi-permeable internalmembrane, which allows perfusion of the cell-matrix construct andgenerates hydrostatic pressure within the cell-matrix construct. In thissystem, the appropriate physiologic hydrostatic pressure is applied tothe cell-matrix construct, which is useful for chondrogenicdifferentiation of the cells.

The term “hypoxia” as used herein refers to a deficiency in oxygen. Inspecific aspects, it refers to oxygen tension that is less than about20%.

The term “joint” as used herein refers to a region in the body whereintwo bones of a skeleton join.

The term “membrane” as used herein refers to a pliable layer of materialthat separates different types and/or areas of biological material. Itmay be comprised of natural and/or synthetic material, and it may bepermeable to substances in solution, for example.

The term “microfluidic scaffold” as used herein refers to a materialthat comprises a system of microchannels.

The term “minimally invasive surgery” as used herein refers toprocedures performed through one or more small incisions in anindividual. For example, in certain aspects minimally invasive surgeryuses specialized techniques, miniature cameras with microscopes, tinyfiber-optic flashlights and/or high definition monitors. For theindividual, minimally invasive surgery means less trauma to the body,less blood loss, smaller surgical scar(s) and less need for painmedication, when compared to conventional open surgery. Individuals aresuited to leave a medical facility sooner after minimally invasivesurgery and return to normal activities sooner than with conventionalopen surgery.

The term “reservoir” as used herein refers to a device that acts as aninjection chamber. In specific embodiments, the type of reservoir may beone that is routinely used in the art to deliver drugs (antibiotics forexample, in case of meningitis or ventriculitis), into the cerebralventricular system (hence the term of “ventriculostomy”), into a vein(chemotherapy for oncologic purpose), or into the subarachnoid spinalspace (morphine for pain relief), for example. It may be considered tobe a kind of drug delivery system, in particular aspects. It iscomprised of several parts: 1) a silicone-based (called “silastic”)material top that allows repeated punctures without losing itswaterproof characteristics; 2) a stainless-steel base that avoids theneedle to injure the underlying tissues; and 3) a silastic end thatconnects to a catheter. The catheter may also be made of silastic. Itsdistal end can be brought to the site and cut at the right size, whileits proximal end is connected to the reservoir's end. The exemplarysystem defines a 1 to 2 cm³ chamber, hence its name of “reservoir”(tank).

The term “scaffold” as used herein refers to a porous biodegradablepolymer construct that supports cell growth and/or migration, forexample.

The term “seeding” as used herein refers to implanting cells in ascaffold. The cells will attach to the scaffold and then grow anddifferentiate in the scaffold.

II. General Embodiments of the Invention

In general embodiments of the invention, there is provided a device andmethods of its use, wherein the device comprises cell-matrix constructof chondrocyte-like cells encapsulated in a multilayered membrane.Although any tissues may be repaired at least in part by methods of theinvention, including any cartilage tissues, in a particular exemplaryembodiment, intervertebral disc cartilage or joint cartilage isrepaired. Exemplary methods of the invention utilize a combination of aliving core and inert core or structure, thereby providing a hybridstructure. In particular aspects of the invention, the living corecomprises a cell-matrix construct of chondrocyte-like cells, such as arederived from HDFs, and the inert structure comprises the living core andis implanted into a patient using a minimally invasive surgicalprocedure, for example.

The present invention provides a method for biological repair ofcartilage using autologous Human Dermal Fibroblasts (HDFs) as cellsourcing. The present invention also provides a device comprising acell-matrix construct of cells, such as chondrocyte-like cells, that areencapsulated in a multilayered membrane. In a particular embodiment, theinvention concerns growth and differentiation of cells in vivo using aspecial device. The chondrogenic differentiation is induced bymechanical stress, and in particular aspects, Intermittent HydrostaticPressure (IHP) and/or fluid shear stress, for example.

A general embodiment of the invention is to use HDFs as cell sourcingfor engineering new cartilage for the intervertebral disc, because thesecells are easy to harvest and to grow. The idea is to inducedifferentiation of these cells into chondrocyte-like cells. There isalready some evidence for chondrogenic differentiation of HDFs intochondrocyte-like cells. However, these studies are only in vitro and thetechnique to differentiate the cells is based on the use of specificgrowth factors, hypoxia, or specific matrix such as aggrecan.

Because of its design, this device allows one or both of the following,for example: 1) diffusion of nutrients and oxygen to the living cells;and/or 2) transfer of the load onto the cells. This mechanical force andespecially the IHP is critical for chondrogenic differentiation offibroblasts. It is known that IHP is the most potent stimulus forinduction and maintenance of the chondrocyte phenotype. Whenchondrocytes are harvested from cartilage to be used to engineer invitro new cartilage, these cells need to be expanded but this causes thechondrocytes to dedifferentiate. It has been shown that IHP canredifferentiate the cells into chondrocytes. People who are usingchondrocytes to engineer cartilage in vitro often use mechanical strainsand especially IHP as inducer of differentiation. However, there isnothing in the literature on the effects of IHP on chondrogenicdifferentiation of HDFs.

In embodiments of the invention, there are at least two components tothe device: 1) cell-matrix construct, wherein the cells (HDFs, forexample) are seeded into a scaffold (and cells that do not attach to thescaffold may be washed away); 2) encapsulating device. In specificembodiments, the in vivo encapsulating device is comprised of twoconcentric membranes, in specific embodiments: 1) an internal membraneis a semipermeable membrane that wraps the cell-scaffold construct (thissemipermeable membrane is permeable to small molecules and so allowsdiffusion of nutrients and oxygen and elimination of wastes, but it isimpermeable to macromolecules such as collagen and glycosaminoglycans,for example; these macromolecules that form the natural extracellularmatrix are then retained within the scaffold); and 2) an externalmembrane is hermetic to fluid but permeable to oxygen, and it isexpandable and inflatable in order to be implanted through a minimallyinvasive posterior surgical procedure (in specific embodiments, whenexpanded it will fit the cavity of discectomy, for example exactly fitthe cavity). The external membrane is filled with medium which nourishthe cells. The fluid enclosed within the envelop forms a fluidenvironment that transfers IHP to the living cells. About the day aftersurgery, when the individual can stand up and begin to walk again, heapplies some load on the spine and especially on the instrumented level.Therefore, the living core receives the right cyclic hydrostaticpressure regimen under physiological load through the envelop that isfilled with medium, which is useful for HDFs growth and conversion.Thus, in certain aspects the individual walks within about one day ofimplantation of the device, about two days, about three days, about fourdays, or about five or more days following implantation of the device.

In specific embodiments, the external membrane filled with medium isconnected to a draining system to regularly change the medium. Thechondrogenic differentiation of HDFs is induced by mechanical stress andespecially Intermittent Hydrostatic Pressure (IHP) and/or fluid shearstress in vitro and then in vivo. Exemplary co-culture conditions are asfollows: high density micromass culture, supplementation with BMP-2,ascorbic acid, and hypoxia, for example.

This invention solves many of the problems in the field. The nutrientsand growth factors are provided to the cell-matrix construct by the insitu medium. It avoids the problem of diffusion of nutrients from thesurrounding natural tissue (endplates) which is usually deficient due todegeneration of these structures. Growths factors important forchondrogenic differentiation of HDFs are added to the medium. Inspecific aspects, HDFs are employed, which avoid the use of invasivetechnique to harvest chondrocytes. HDFs, or any other cells, arepre-differentiated in vitro for a short period of time and continue togrow and differentiate in vivo. The encapsulating device with itsexternal envelop filled with fluid will provide the physiologic loadingand compressive forces ideal for chondrogenic differentiation of HDFs.

III. The Hybrid Construct

The invention employs a hybrid construct for repair of cartilage in ajoint, such as an intervertebral disc. Exemplary embodiments of thehybrid construct are described herein, and in certain aspects the hybridconstruct is an implantable device, for implantation into a mammal, suchas a human, dog, cat, horse, pig, sheep, goat, and so forth. Inparticular aspects, a hybrid construct is comprised of at least a livingcore, comprising cells and a scaffold, and an inert structure.

A. Cells/Scaffold Composition

The living core, which may be referred to as the cells/scaffoldcomposition, is a cell-matrix construct and comprises cells seeded in ascaffold (which may be referred to as a matrix). In a specificembodiment, the scaffold comprises alginate beads; a microfluidicscaffold (the Microfluidic scaffold could be made of any biodegradablebiopolymer [organic biodegradable polymers: poly(L-lactic acid) (PLA),poly(glycolic acid) (PGA), poly-lactic-co-glycolic acid (PLGA) naturalhydrogels (collagen, HA, alginate, agarose, chitosan, combinationcollagen/HA, chitosan/GAG, collagen/GAG); and/or synthetic hydrogels(Poly(ethylene oxide), (PEO), poly(vinyl alcohol) (PVA), poly(acrylicacid) (PAA), poly(propylene fumarate-co-ethylene glycol) (P(PF-co-EG))],for example. In specific embodiments, cell adhesion ligands such aspeptides or polysaccharides are employed. The peptide sequences may becapable of binding to cellular receptors. These peptides could comprisethe exemplary amino acid sequences arginine-glycine-aspartic acid (RGD),argininine-glutamic acid-aspartic acid-valine (REDV),tyrosine-isoleucine-glycine-serine-arginine (YIGSR), orisoleucine-lysine-valine-alanine-valine (IKVAV) and may be attached tothe scaffold, wherein the ligands and/or growth factors may beincorporated to regulate cell fate. In fact, the growth factors can beincorporated in the scaffold or included in the medium in the externalmembrane, for example. The scaffold materials may be biodegradable, andthe rate of biodegradation can be manipulated.

In accordance with the invention and as explained above, HDFs aredifferentiated into chondrocyte-like cells under mechanical stresseither in vitro or in vivo or both in vitro followed by in vivo, forexample. As explained above, important co-culture conditions includehigh cell density culture; growth factors (BMP-2); and/or ascorbic acid,for example. HDFs can also be differentiated into chondrocyte-like cellsunder low oxygen tension and culture on aggregan with insulin growthfactor one (IGF-I). As aforementioned, bioreactors are used to induce invitro proliferation and differentiation of HDFs. The inert structure ofthe present invention is used to induce in vivo differentiation, inparticular aspects of the invention. HDFs in alginate beads or HDFsseeded in a microfluidic scaffold or HDFs seeded in any other polymericscaffold are encapsulated in a semi-permeable membrane that is part ofan inert structure, in specific embodiments of the invention. A functionof the semi-permeable membrane is to encapsulate the chondrocyte-matrixconstruct to concentrate the production of ECM proteins. This membraneallows the passage of O₂, nutrients/waste, and CO₂, for example.

In specific embodiments, scaffold refers to a porous biodegradablepolymer construct to support cell growth and/or migration. This materialis non-toxic, biocompatible and biodegradable, in specific embodiments.

In exemplary embodiments, alginate is employed for the scaffold.Alginate is a natural polysaccharide isolated from seaweed. It is apolysaccharide composed D-mannuronate and L-guluronate monomers. Whencrosslinked with calcium ions, it forms a gel that is biocompatible,biodegradable. Alginate is well established as matrix material fortissue within regenerative medicine. It has been used more widely thanother hydrogels to assess in vivo potential of hydrogel scaffolds forcartilage engineering. Macrobeads of alginate (1-3 mm in size) ormicrobeads of alginate (250-500 μm) can be used in this invention.Microbeads of alginate are preferred. These smaller beads have theadvantage of a higher surface to volume ratio allowing good transport ofessential nutrients, they are also less fragile. Alginate isbiocompatible and approved by the U.S. Food and Drug Administration forhuman use.

HDFs may be seeded in alginate macrobeads (as described below) orpreferentially in alginate microbeads. There are different techniquesknown in the art to generate alginate microbeads. There are usuallyproduced by electrostatic droplet generation. For example, HDFs can beseeded in alginate microbeads as follows. Alginate powder (Sigma, StLouis, Mo.) is dissolved in WFI water at a concentration of 2.2% w/w andthen mix with a suspension of HDFs in culture medium to obtain finalconcentrations of 1.5% w/w alginate and 10⁷ cell /ml. Alginatemicrobeads are then produced by electrostatic droplet generation. Inbrief, cell/alginate suspension is extruded through a positively chargedblunt stainless steel needle at a constant flow rate of 14.0 ml/h by asyringe pump and resulting droplets are collected in a gelling bath (1.5w/v CaCl₂). As Na⁺ ions are exchanged with Ca²⁺ ions, alginate dropletsharden and form insoluble microbeads with entrapped cells. Themicrobeads are left for 30 min in the gelling bath in order to completegellation.

Microfluidic scaffolds may also be employed, in particular embodiments.They are complex scaffolds with micron-scale resolution. These scaffoldspresent a network of micro-channels that allow fluid flow within thescaffold. This network of micro-channels helps to provide both nutrientsand soluble factors to distinct sections of the scaffold. Thesescaffolds can be made of different biopolymers. They can be made ofsynthetic polymers such as polyglycolic acid (PGA), polylactic acid(PLA), polylactic-co-glycolic acid (PLGA); synthetic hydrogels such aspoly(ethyleneoxide) (PEO), poly(vinyl alcohol) (PVA), poly(acrylic acid)(PAA), poly(propylene furmarate-co-ethylene glycol (P(PF-co-EG), or ofPoly(glycerol-Sebacate) (PGS) that is a biodegradable elastomer. In theinvention, this microfluidic scaffold is encapsulated with asemi-permeable membrane. This semi-permeable membrane allows theperfusion of medium containing nutrients and growth factors within thescaffold. By circulating within the network of micro-channels, themedium will apply fluid shear stress on the cells seeded in thisscaffold. This mechanical force is critical for chondrogenicdifferentiation of HDFs.

B. The Inert Structure

In the invention, the hybrid construct employs an inert structure aspart of its composition. Functions of the inert structure may bebiological (delivery of nutrients and/or growth factors) and/ormechanical (to transfer mechanical forces, such as onto thecells/scaffold composition; such forces may include IHP and/or Fluidshear stress), for example. The inert structure may function as an “invivo bioreactor” by transferring mechanical strain and by providingmedium (by perfusion through the semi-permeable membrane) to thecells/scaffold composition.

In certain embodiments, functions of the inert structure include one ormore of the following: 1) to hermetically encase the living core; 2) toact as a semi-permeable membrane by allowing certain molecules (forexample nutrients, growth factor, etc.) to pass through it by diffusion(and occasionally specialized “facilitated diffusion”) under certainphysico-chemical conditions (for example, hydrostatic pressure, osmoticconcentration, temperature, etc.); 3) to transfer the load and to sharethe dynamic mechanical stress (hydrostatic pressure) to the livingcompartment acting as an inducer of cell differentiation; and/or 4) toact as an in vivo bioreactor.

The inert structure may be considered an encapsulating device, inspecific embodiments. For certain embodiments, it is designed to applymechanical stress on the cells seeded in the three-dimensional scaffoldcomposition. The external membrane of the encapsulating device is filledwith fluid (medium). The fluid enclosed within the envelop forms a fluidenvironment that transfers the cyclic hydrostatic pressure to the livingcells. When the patient stands up, for example, he applies some load onhis spine that is transferred to the living cells through the externalenvelop that is filled with fluid. This membrane provides thephysiologic loading and compressive forces suitable for chondrogenicdifferentiation of cells such as HDFs. In the case of cells embedded ina microfluidic scaffold, the medium circulating within themicro-channels also apply fluid shear stress on the cells. This fluidshear stress is another force that induces chondrogenic differentiationof cells.

In specific embodiments, the membrane is generally balloon-shaped, andin additional embodiments the membranes are generally concentrical withone another. In further specific embodiments, the inert structurecomprises two expandable balloon-like bio-polymers, namely, internalballoon “I,” which is enclosed within an external balloon “E”. Hence,the inert structure comprises two concentric envelopes capable of beingsuccessively inflated and having inflation activity. In certain aspects,a number X of membranes may be utilized in the device, wherein X is anywhole integer greater than one. That is, X balloons may be installedconcentrically as with layers in an onion, each of them defining a spacewith a specific function (for example, for waste, media, oxygen, and/orfor connecting the graft to natural tissue).

In one embodiment, the external balloon, layer or envelope “E” comprisesa biocompatible resilient, inflatable, hermetic, expandable, and/orresorbable (time T₁, wherein T₁ is the time for complete resorption of“E”) material that is able to be sealed once installed in the cavity. Inspecific embodiments, external balloon “E” is capable of having or hasone or more of the following activities: 1) to receive a second internalballoon or layer or envelope “I” enclosing the cells (in the form ofcell-matrix construct, or cell solution or graft); 2) to be inflatedwith a media (for example, liquid) or to expand its wall (for example,via swelling) in order to fill the cavity resulting of the discectomy;and 3) to close the annulus defect to prevent it from “herniating” orcoming out from the inter-somatic space through the tenotomy incisiononce the construct is under load.

In one embodiment, the internal balloon or layer “I” comprises abiocompatible, resilient, inflatable, semi-permeable, and/or resorbable(time T₂<T₁, wherein T₂ is the time for complete resorption of “I”)material that is able to seal the living core once installed into theexternal layer. The internal balloon (envelop, membrane, or layer) “I”is capable of having or has the following activities: 1) to hermeticallywrap up the living core; 2) to act as a semi-permeable membrane byallowing certain molecules (for example, nutrients, growth factors,etc.) to pass through it by diffusion (and occasionally specialized“facilitated diffusion”) under certain physico-chemical conditions (forexample hydrostatic pressure, osmotic concentration, temperature, etc.);and 3) to transfer the load to the living core so as to share thedynamic mechanical strain therewith, thereby acting as an inducer ofcell differentiation.

In accordance with an aspect of the invention, the combination of anexternal compartment media (such as a liquid, for example) or swelledwall (such as hydrated hydrogel, for instance) “E” and the internalsemi-permeable envelope provide a delivery system of nutrients andgrowth factors capable of feeding an inner living core. These envelopesalso transfer the mechanical forces, including hydrostatic pressure tothe living core.

The inert structure is an encapsulating device intended to wrap up, feedand differentiate a living core made of cells, such as HDFs.

In a preferred embodiment, the inert structure comprises two expandableballoon-like bio-polymeric membranes, namely, internal membrane “I”which enclosed within an external membrane “E”. Hence, the inertstructure comprises two concentric envelops intended to be successivelyinflated. At the rest position, the two envelopes “I” and “E” are flat,deformable, shaped and fit one another. Both can be sealed onceimplanted. The inert structure composition may be determined by thechoice of tissue engineering system, in specific embodiments.

The external envelope “E” comprises a material that is inflatable (inorder to be implanted flat through a minimally invasive posteriorapproach, then loaded with the living core, and then inflated with themedia solution); resilient (to transfer load sharing onto the livingcore); expandable (to allow its expansion and fill the cavity resultingof the discectomy); permeable to O₂ but hermetic to fluids: relativehypoxia is a useful parameter of HDFs conversion, but O₂ tension withinthe natural disc is appropriately low; biodegradable (to allow the graftto reconnect with the natural remaining disc); biocompatible (tominimize inflammatory reaction); resorbable (time T1); or a combinationthereof.

“E” may be positioned in a joint, for instance, into the cavityresulting of the curettage of an inter-somatic space between a pair ofadjacent vertebrae and within the remaining discal tissue, in specificembodiments. It also may be mechanically able to maintain the discheight under loading. In additional embodiments, “E” receives a secondinternal balloon “I” enclosing the living core. “E” may be inflated witha fluidic solution (for instance the media) to extend in the chamber(cavity resulting of the discectomy) peripherally up to the remainingdiscal tissue and fill the cavity. “E” is configured such that it allowschanging of the media (removal of metabolic wastes and/or replenishmentof nutrients and/or growth factors, for example), such as under anisobaric regimen, for example. “E” acts as an in vivo bioreactor bytransferring the load sharing onto the living core, for example withcyclic hydrostatic pressure (which is useful for differentiating cellsinto chondrocyte-like cells), in certain aspects. In particularembodiments, the configuration of “E” produces relative hypoxia due toits characteristics (Hypoxia or hypoxia-mimicking agent, as lactate,induces HDFs conversion in chondrocytes-like cells). “E” may also closethe annulus defect (tenotomy opening) to prevent it from “herniating” orcoming out from the inter-somatic space through the tenotomy incisiononce the construct is under load.

In certain aspects of the invention, the internal membrane “I” comprisesa membrane that is biocompatible; resilient; inflatable (while the mediais consumed, the living core grows and expands to the inner wall of theexternal membrane); semi-permeable (controlled release system fornutrients, growth factors, etc.); biodegradable (so as not to interferewith the long-term properties of the repaired tissue); and resorbable(time T₂<T₁). E” must resorb after “I” not only to avoid the leakage andthe lost of the media while the living core is not mature yet, but alsoto keep the fragile “I” away from any direct mechanical strain). Inother certain aspects, “I” hermetically wraps up the living core; actsas a delivery system of nutrients and growth factors capable of feedingan inner living core through a semi-permeable membrane by allowingcertain molecules (for example nutrients, growth factor etc.) to passthrough it by diffusion (and occasionally specialized “facilitateddiffusion”) under certain physic-chemical conditions (for examplehydrostatic pressure, osmotic concentration, temperature, etc.)

These two membranes (“E” and “I”) define 2 volumes V_(E) and V_(I).These two distinct volumes may have different shapes (spherical,cylindrical, conical, etc.) depending of the contour of theinter-vertebral cavity and the load sharing. In specific embodiments,the device conforms to the shape of the cavity.

Volume V_(E) is defined as the space that separates membrane “E” frommembrane “I”. It comprises nutrients and growth factors (media) to bedelivered to the cells, in specific embodiments, such as through thesemi-permeable membrane “I”. It also acts as a load-bearing structurecapable of transferring mechanical strain, for example the cyclichydrostatic pressure regimen or the high fluid shear stress (due to itshigh content water) to the living core (which induces chondrogenicdifferentiation of cells, such as HDFs).

Volume V_(I) is defined as the space that is outwardly limited by theinternal semi-permeable membrane “I” and comprises the living core madeof chondrocyte-like cells, such as cells derived from HDFs.

Until the living core has become viable (e.g. capable of selfmaintenance) the media enclosed in V_(E) may be regularly changed inorder to remove any toxic wastes accumulated due to the metabolism (freeradicals and/or lactic acid, for example), as well as any other cellularscraps or debris as a result of the cellular growth. Such a changeallows replenishment of its contents with nutrients and/or growthfactors. In specific embodiments, this procedure is performedperiodically, such as one or more times per week or month, for exampleat least once a week, such as twice a week. In additional specificembodiments, it requires to equip “E” with an additional feature fordraining V_(E). This draining system may be made of one or more tubesand one or more reservoirs, in certain aspects, and in particularembodiments it comprises two tubes and two reservoirs. The first tubemay be employed to remove the used media, and the second tube may beemployed to inject the new media. Each of these tubes (or catheters)comprises a proximal end that hermetically connects to V_(E) and adistal end that connects to a reservoir. These catheters could be madeeither of the same material as “E” or of silicone rubber, for example.Their length may be of any suitable length so long as they can span fromthe reservoir to the device. They may be comprised between about 10 and15 centimeters, and is pre-operatively set up by cutting their distalend at the appropriate length according to the depth of the operativesite and the anatomical data (patient's morphology). Their outerdiameter may be of any suitable length, but in specific embodiments theyare about 2.5 millimeters in length, such as in order to be small enoughto exit from the tenotomy aperture, not to compress or injure theadjacent root, and allow a 1.2 millimeter inner diameter.

The tubes may be implanted at the end of a discectomy procedure, afterimplantation, inflation and sealing of the bio-reactor, and before skinclosure. They may be connected to the distal end of each tube(catheter). Then, each reservoir may be subcutaneously positioned sothat it can be reachable by a needle from the skin (percutaneouspuncture).

In one embodiment, the engineered living core is pre-encapsulated with“I” and then slid into “E”. While the media is consumed, the living coreexpands to the inner wall of the envelope “E”. The envelop “E” resorbsand the graft reconnects with the natural remaining disc.

1. The Internal Semi-Permeable Membrane

The internal envelop comprises the living core, includes a controlledrelease system (in order to allow the feeding of the living core withthe media through its semi-permeability characteristics), is expandable(while the media is consumed, the living core expands to the inner wallof the external membrane), and/or is biodegradable (so as not tointerfere with the long-term properties of the repaired tissue), forexample.

In specific embodiments, the internal membrane is a semi-permeablemembrane that wraps the cell-scaffold composition. This semi-permeablemembrane is permeable to small molecules and so allows diffusion ofnutrients and oxygen and elimination of wastes; but this membrane isimpermeable to macromolecules such as collagen and glycosaminoglycans.These macromolecules that form the natural extracellular matrix are thenretained within the scaffold. This membrane also isolates thecell-matrix construct from the host environment and protects frominflammatory and immunological response of the host against thebiopolymeric scaffold.

Various polymers and polymer blends can be used to manufacture thismembrane, including but not limited to, polyacrylates (including acryliccopolymers), polyvinylidenes, polyvinyl chloride copolymers,polyurethanes, polystyrenes, polyamides, cellulose acetates, cellulosenitrates, polysulfones (including polyether sulfones), polyphosphazenes,polyacrylonitriles, poly(acrylonitrile/covinyl chloride), PTFE, as wellas derivatives, copolymers and mixtures of the foregoing.

In one embodiment, the semi-permeable membrane is generated bypolyelectrolyte complexation: polyanion (PA) and polycation (PC) viainteractions between oppositely charged polymers form polyelectrolytecomplex (PEC). The anionic component may be a biocompatible polymer,such as, but not limited to, sodium alginate, cellulose sulfate,carboxymethyl cellulose, or hyaluronic acid, and the cationic componentmay be made of a polymer, such as, but not limited to, chitosan,poly(L-lysine, poly(L-ornithine),Poly(methylen-co-guanidine),poly(vinylamine), poly(ethylenimine), poly(DADMAC), orpoly(N-vinylpyrrolidone), for example.

To carry out the encapsulation of the cell-matrix construct with asemi-permeable PEC membrane, cell matrix-construct is first immersed inthe anionic solution and then in the cationic solution. After a reactiontime that varies depending on the nature of the anionic and cationiccomponents, a mechanically stable semi-permeable membrane is formed.Depending on the reaction conditions (polymer concentration, reactiontime), the scaffold is either tightly wrapped within the membrane orseparated from it by a gap.

Volume V_(I), is defined as the space that is outwardly limited by theinternal semi-permeable membrane “I” and comprises the living core madeof chondrocyte-like cells derived from HDFs, for example.

2. The External Membrane

The external membrane may be expandable, elastic and/or inflatable inorder to be implanted through a minimally invasive posterior surgicalprocedure and when expanded to fit exactly the cavity of discectomy.This membrane is hermetic to fluid but permeable to oxygen and is filledwith medium that provides nutrients and growth factors to the cells. Thefluid enclosed within the envelop forms a fluid environment thattransfers IHP to the living cells. When the patient stands up, heapplies some load on his spine that is transferred to the living cellsthrough the membrane that is filled with fluid. This membrane ismechanically resistant to support the load.

The external membrane may be made of a biocompatible, biodegradablepolymer. Various polymers can be used to manufacture this membraneincluding, but not limited to, polyglycolic acid (PGA), polylactic acid(PLA), polylactic-co-glycolic acid (PLGA), poly-e-caprolactone (PCL),polyurethane (PU), polydioxanone (PDO), polyethylenes, poly (glycerolsebacate) (PGS) as well as derivatives, copolymers and mixtures of theforegoing. In one embodiment the membrane is comprised of an expandable,biocompatible, biodegradable polyurethane.

This membrane is in direct contact with the host-surrounding tissue andis biocompatible to avoid inflammatory reaction of the host. Differenttechniques can be used to improve the membrane biocompatibility such as,but not limited to, coating the membrane with hyaluronic acid.

IV. Cells Utilized in the Invention

In certain embodiments of the invention, any cell may be employed solong as the cell is capable of differentiating into a chondrocyte orchondrocyte-like cell. In specific embodiments, the cell is in fact achondrocyte, although it may be derived from a stem cell (for example,mesenchymal stem cell), or a fibroblast cell, such as a dermalfibroblast, tendon fibroblast, ligament fibroblast, or synovialfibroblast. Autologous cells may be utilized, although in alternativeembodiments allogeneic cells are employed; in specific embodiments, theallogeneic cells have been assayed for disease and are consideredsuitable for human transmission. In certain aspects of the invention thecell or cells are autologous, although in alternative embodiments thecells are allogeneic. In cases wherein the cells are not autologous,prior to use in the invention the cells may be processed by standardmeans in the art to remove potentially hazardous materials, pathogens,etc. In particular aspects, the cells may be transfected with one ormore nucleic acids, such as transfected with a growth factor, includingBMP-2 -4, -6, and/or -7, for example.

In particular aspects, chondrocyte-like differentiation of human dermalfibroblasts may be facilitated by employing one or more of thefollowing: seeding cells in alginate; seeding cells in extracellularmatrix proteins such as aggrecan or perlecan, hypoxic conditions (suchas hypoxia or one or more hypoxia-mimicking agents, for example lactate,Desferrioxamine mesylate (DFX), cobalt chloride (CoCl₂), or nickel, forexample); high density micromass culture; presence of one or more growthfactors (including, for example, bone morphogenetic proteins (BMPs),including at least BMP-2; transforming growth factor beta (TGF-β);insulin growth factor one (IGF-I); and fibroblast growth factors (FGFs)and particularly basic fibroblast growth factor (bFGF) and FGF-2,platelet-derived growth factor (PDGF), cartilage-derived morphogeneticprotein (CDMP)]; presence of ascorbic acid, dexamethasone, parathyroidhormone-related protein (PTHrP), hedgehog proteins: sonic hedgehog (SHH)and Indian hedgehog (IHH)). Culture under mechanical stress may beemployed. High density micromass culture is a culture technique thatmimics the cellular condensation stage that occurs during the onset ofcartilage formation in the developing limb.

In particular aspects of the invention, human dermal fibroblasts areemployed, at least because they can be non-invasively harvested, such asfrom a punch biopsy as little as about 3 mm in diameter (in specificembodiments) from skin, for example a circular biopsy skin specimen.Also, human dermal fibroblasts can expand easily in culture and candifferentiate into chondrocyte-like cells under particular cultureconditions.

In accordance with the invention, autologous HDFs are harvested frompunch biopsy of skin tissue (6 mm) from the patient. In the laboratory,subcutaneous fat and deep dermis are dissected away with scissors. Theremaining tissue is minced and incubated overnight in 0.25% trypsin at4° C. Then, dermal and epidermal fragments are mechanically separated.The dermal fragments of the biopsy are minced and the pieces are used toinitiate explant cultures. Fibroblasts harvested from the explants aregrown in Dulbecco' s MEM (DMEM) with 10% calf serum at 37° C. in 8% CO₂.These cells are expanded before being differentiated into chondrocytes,in particular aspects.

Some aspects may employ HDFs purchased commercially, such as fromlaboratories (such as Cascade Biologics). The cells can be adult HDFs orneonatal HDFs. Neonatal foreskin fibroblasts are a very convenientsource of cells, for example. These cells are used commercially and arereadily available and easy to grow.

V. Growing and Differentiating Cells into Chondrocytes orChondrocyte-Like Cells

Mechanical stress/strain are important factors for chondrogenesis. Thepresent method uses one or more mechanical strains and, in particularembodiments, uses intermittent hydrostatic pressure (IHP) as inducer ofchondrogenic differentiation of HDFs. IHP is known as a potent stimulusfor induction and maintenance of the chondrocyte phenotype. Recentstudies have demonstrated that IHP stimulates chondroinduction of murineembryonic fibroblasts cultured with BMP-2. IHP can also inducechondrogenic differentiation of HDFs. It is known that HDFs candifferentiate into chondrocyte-like cells under low oxygen tension.Therefore, in accordance with an embodiment of the present invention,mechanical stress, especially IHP and shear fluid stress, inducechondrogenic differentiation of fibroblasts cultured in a threedimensional matrix and low oxygen tension, for example.

Mechanical stress can be performed in vitro, in vivo, ex vivo, in vitrofollowed by in vivo, or a combination thereof. In an embodiment, thedifferentiation will be initiated in vitro, and the chondrocyte-likecells seeded in the matrix will be then implanted in vivo and continueto grow and differentiate. The inert structure is intended to provide aphysiologic loading regimen to induce in vivo differentiation of HDFs,in specific aspects of the invention.

In specific aspects of the invention, cells are induced to undergodifferentiation into chrondrocytes or chondrocyte-like cells. Suchdifferentiation may occur prior to in vivo delivery, such as on ascaffold, or subsequent to delivery in vivo. In specific embodiments,the cell is subjected to conditions to facilitate differentiation intochondrocytes. In a further specific embodiment, a condition comprisesmechanical stress. Regulation of genes by mechanical forces has beenstudied extensively for vascular endothelial cells and chondrocytes thatare obviously subjected to high fluid shear or pressure load. Inspecific embodiments of the invention, mechanical stress stimulateschondrogenic differentiation of HDFs. Such mechanical stress may be ofany kind, although in specific embodiments it comprises hydrostaticpressure and/or fluid shear stress. In additional specific embodiments,the stress is constant or intermittent.

In the present invention, mechanical stress, especially cyclichydrostatic pressure and shear fluid stress induce chondrogenicdifferentiation of fibroblasts seeded in a three dimensional matrix. Thechoice of the co-culture conditions to stimulate the chondrogenicdifferentiation of HDFs is based on data known in the art. Differentexemplary factors such as high cell density culture, culture with BMP-2and ascorbic acid, culture in low oxygen tension are known to stimulatechondrogenesis and are used solely as examples in the invention asco-factors in addition to the mechanical stress.

Chondrocytes from intervertebral discs are difficult to harvest. Theautologous cells are obtained from the patient's disc and so requires aninvasive procedure (back surgery) to perform a biopsy. If cells areharvested from a healthy disc, it jeopardizes the functioning of anormal disc. If cells are harvested from a damaged disc during thediscectomy, it provides abnormal cells from a degenerated tissue.Moreover, chondrocytes are difficult to expand in culture because theyde-differentiate. Chondrocytes from other cartilages such as the elasticcartilage from the ear is easy to harvest but produces only hyalinecartilage and not fibro-cartilage as in the disc. Stem cells that areusually used for tissue engineering also have some disadvantages,because they require a bone marrow biopsy. A large quantity of cells isneeded for tissue engineering, and it is difficult to obtain asufficient quantity of adult stem cells.

The rationale for using autologous HDFs as a means of cell sourcingfollows from the following: 1) HDFs can be non-invasively harvested froma punch biopsy as little as a 3.0 mm diameter circular skin specimen,for example; 2) the risk of contamination from another donor (such asHepatitis B Virus, Human Immunodeficiency Virus, Creutzfeldt-Jakobdisease, etc.) does not exist.; and 3) HDFs can expand easily in cultureand differentiate into chondrocyte-like cells under particular cultureconditions. Other fibroblast populations could be used, such as tendonor ligament, for example. In an embodiment, autologous fibroblasts arepreferred.

The choice of the culture conditions to stimulate the chondrogenicdifferentiation of HDFs is based on data known in the art. Differentfactors support chondrogenesis, such as, for example, high cell densityculture, culture with BMP-2 and ascorbic acid, and seeding cells inalginate matrix. In vitro growth and/or differentiation of the cells inthe cells/scaffold composition may comprise at least two or more daysprior to use in vivo. In certain cases, the cells may be checked ormonitored to ensure that at least some of the cells are dividing. Cellsthat are not dividing and/or that are not affixed directly or indirectlyto the scaffold may be removed.

In other embodiments, HDFs are embedded in hydrogel that in specificembodiments is a natural hydrogel such as collagen, hyaluronic acid(HA), a combination of collagen/HA, alginate, chitosan; a synthetichydrogel such as poly(ethyleneoxide) (PEO), poly(vinyl alcohol) (PVA),poly(acrylic acid) (PAA), poly(propylene furmarate-co-ethylene glycol(P(PF-co-EG), and polypeptides, or other biodegradable polymers such aspoly(L-lactic acid) (PLA), poly(glycolic acid) (PGA),poly-lactic-co-glycolic acid (PLGA); or a combination of any of theseabove mentioned polymers. A cyclic hydrostatic compression is thenapplied using any suitable in vitro bioreactor in the art.

VI. Methods of Repairing Damaged Cartilage

In certain embodiments, the invention includes methods of repairing anydamaged cartilage, although in particular aspects the cartilage is in anintervertebral disc or any joint. Generally, for disc embodiments whenan intervertebral disc must be removed from between two adjacentvertebrae, e.g. in the lumbar spine, it is less invasive to surgicallyproceed posteriorly from the back of the patient. This minimallyinvasive procedure allows one to proceed with the curettage of theinter-somatic space through a small aperture within the annulus(tenotomy) for removing the degenerated fragments of the disc's nucleus.As the annulus fenestration is small, the present invention provides anintervertebral construct that is slid through the aforementionedincision and then expanded into the room generated by the nucleusremoval within the inter-somatic space. The removal of the damaged discand the installation of the construct are performed in the sameposterior approach.

As mentioned above, the inert structure is made of two expandableballoons “I” and “E”. At the rest position, the two balloons “I” and “E”are flat, deformable, shaped and fit one another. Once the balloon “I”is inside the balloon “E”, they are both installed into theintervertebral space through the annulus aperture, and then successivelyinflated so as to define two distinct volumes (V_(E)>V_(I)) of shapes(spherical, cylindrical, conical, etc.,) depending on the contour of theinter-vertebral cavity and the load sharing, for example.

In particular aspects, the first balloon to be filled is the internalballoon “I” regardless of the volume of the remaining cavity. VolumeV_(I) represents the core of the construct that receives and houses theliving core. Once filed with the living core, the balloon “I” ishermetically sealed. That is, once the envelope “I” is placed into theenvelope “E”, both are positioned into the intervertebral space throughthe annulus aperture, and then successively inflated. “I” is the firstto be instrumented with the implantation of the living core, and thensealed. Then, the external balloon “E” is inflated with the mediasolution until its volume V_(E) gets a contour that mates with, orfollows, the inner surface of the remaining part of the natural discafter the curettage thereof. This inner surface of the remaining disccan be either the remainder of the nucleus tissue or the inner wall ofthe natural annulus, depending how extensive the curettage has beenperformed.

In a second embodiment to install the intervertebral construct, “E” ispositioned into the intervertebral space, then “I” is placed into “E”,and they are both filled successively as aforementioned. In a thirdembodiment, “E” is positioned into the discectomy cavity, then thepre-encapsulated living core is placed into “E”, and then “E” is filledwith the media.

The volume of the cavity resulting from the discectomy may be evaluatedprior to the installation of the external balloon “E” such that properfluid volume can be selected and injected. The cavity volume could be,for instance, measured by introducing a fluid (e.g., water) therein,until the cavity is filled therewith, and by then withdrawing the fluidfrom the cavity by way of a syringe, thereby substantially exactlymeasuring the cavity's volume.

In certain aspects, the inert structure composition depends on thechoice of tissue engineering system that relies on material offabrication, pore characteristics, absorbability and mechanicalproperties, for example, such as non-degradable polymers, degradablepolymers or naturally derived hydrogels (for example collagen, fibrin,agarose, alginate, etc.).

The living core or compartment (V_(I)) is made of chondrocyte-like cellsderived from autologous Human Dermal Fibroblasts (HDFs), for example,such as those harvested from skin of the patient and seeded in ascaffold (such as alginate beads, or micofluidic scaffold, or any otherpolymeric scaffold) and fed from the supportive compartment (V_(E)). Theadvantage of this hybrid construct combining both an inert biomaterialacting as a nutrients delivery system and living cells easily harvestedfrom skin is that it is capable of self maintenance or remodeling andmay restore the disc function using a minimally invasive posteriorsurgical approach. Volume V_(E), is defined as the space that separateslayer “E” from layer “I” that comprises nutrients and growth factors(media) to be delivered to the cells (delivery system). This volume canbe the result either of its filling by the liquid media, or its swellingfrom its wall (expandable hydrophilic biomaterial as hydrogel, forinstance) after having been hydrated (the media is made of a high ratioof water).

Growth factors may be delivered through the semi-permeable internalmembrane “I”. Example of growth factors include, for example,cartilage-derived morphogenetic protein (CDMP), bone morphogeneticproteins (BMPs), transforming growth factor beta (TGF-β), and insulingrowth factor one (IGF-I), fibroblast growth factors (FGFs),platelet-derived growth factor (PDGF), for example.

Mechanical strain, such as high fluid shear and/or pressure load, istransferred on internal layer “I”, and therefore on V_(I) through theexternal layer “E” and the external area V_(E). This mechanical straininduces chondrogenic differentiation of the cells inside the internallayer.

The draining system is then installed, wherein each catheter exitingfrom the intervertebral space through the tenotomy aperture is carefullykept away from the adjacent root, or at least positioned along the rootwithout any harmful conflict.

A trans-muscular path is performed using an introducer from theoperative site to a subcutaneous location distant from the skinaperture. Each tube is “tunnelized” into the aforementioned muscularpath then connected to the corresponding reservoir. The two reservoirsare distant from the medial skin incision, positioned at 2 or 3centimeters from the medial line, subcutaneously placed so that they areeasily palpable and identifiable. Each skin incision is closed.

As it is usual to proceed after such minimally invasive posteriorapproach, the patient is asked to stand up as early as the day after thesurgery, and can begin to walk again. Therefore, the implant receivesthe right cyclic hydrostatic pressure regimen under physiological load,which is critical for HDFs growth and conversion.

Periodically, such as one or more times per week or month, the media maybe changed The draining system allows one to provide the volume V_(E)with the appropriate amount of new media in order to continue to supplythe living core, but also to maintain the adequate volume and thereforethe right pressure regimen. The individual lies face-down. Eachreservoir is simultaneously punctured with a needle. A syringe isplugged in on each of these needles and the new media is slowly injectedby pushing down the piston while the same amount of fluid issimultaneously removed from the other syringe by pulling up, so that theinternal pressure remains almost the same, and avoids the volume V_(E)to collapse, or, at the contrary, to deliver too high of a pressure tothe volume V_(I), which could cause irreversible damage to the livingcore. The procedure is stopped when the color and the aspect of theexiting fluid has become identical to the entering fluid, for example.Samples from the removed used media may be taken for bacteriological,pathological and chemical purposes.

When the living core is capable of self maintenance and has filled theroom of the discectomy, both tubes and reservoirs can be removed.Alternatively, only one or both reservoirs can be removed under localanesthesia while the tubes are tied at their distal end. In anotheralternative embodiment, both can be let in place.

In specific embodiments, a follow-up MRI is performed, such as withinweeks or months of the surgery (for example, about 6 weeks aftersurgery) to assess the graft growth and to document the disc healing

In another embodiment, the engineered living core is pre-encapsulatedand released as aforementioned.

These foregoing functions are provided by the inert structure of theinvention that relies on two concentric membranes with two differentskills. The external envelop is mechanically able to maintain discheight under loading; is inflatable (in order to be implanted through aminimally invasive posterior approach and receive the media solution);is resilient (to transfer load sharing onto the graft); is expandable(to allow its swelling and fill the cavity resulting of the discectomy);is hermetic (to avoid any leak of the media, extrusion of scar tissuesinto the spinal canal, or recidivism of herniation through the annulusdefect—tenotomy—); is biodegradable (the envelop resorbs to allow thegraft to reconnect with the natural remaining disc); and isbiocompatible (to minimize inflammatory reaction). It may be drainedwith one or several catheter(s) connected to one or several Rickhamreservoir(s) subcutaneously inserted at the end of the surgicalprocedure, for example.

These reservoirs are intended to remove any toxic wastes accumulatedwith the metabolism (free radicals or lactic acid, for example), as wellas any other cellular scraps consecutive to the growth. They also allowproviding the volume V_(E) with the appropriate amount of new media inorder to continue to supply the living core, but also to maintain theadequate volume and therefore the right pressure regimen. They areremoved when the living core is capable of self maintenance and hasfiled the room of the discectomy.

It should be noted that the various components and features of thehybrid structure, as well as the method of repairing damaged cartilageand method for growing HDFs into chondrocyte-like cells described above,can be combined in a variety of ways so as to provide other embodimentswithin the scope of the invention.

VII. Alternative Embodiment of the Invention

In another embodiment, instead of having two generally spherically (forexample) concentric envelopes, the device could be made of a uniqueexternal envelope “E” with the same aforementioned characteristics(especially expandability and/or inflatable properties), and receives anunwrapped living core (non-encapsulated nor wrapped up with a membrane).Actually, in this embodiment, this living core is a cell matrixconstruct and is directly positioned into “E”. Then, the volume V_(E) isexpanded with the media liquid solution until mating the cavity.

Thus, in another embodiment, instead of having two “concentric”balloons, the device is comprised of a unique external balloon “E” withthe same aforementioned characteristics (especially expandability and/orinflatable properties) for housing the engineered living core. Once theliving core is released within the membrane “E”, the volume V_(E) isexpanded with the media liquid solution until the membrane “E” reachesthe boundaries of the cavity. Neither barrier nor membrane wrap up thegraft anymore. While the media is consumed, the living core expands tothe inner wall of the balloon/layer/membrane “E”. The envelop resorbsand the graft reconnects with the natural remaining disc.

Examples

The following examples are included to demonstrate preferred embodimentsof the invention. It should be appreciated by those of skill in the artthat the techniques disclosed in the examples which follow representtechniques discovered by the inventor to function well in the practiceof the invention, and thus can be considered to constitute preferredmodes for its practice. However, those of skill in the art should, inlight of the present disclosure, appreciate that many changes can bemade in the specific embodiments which are disclosed and still obtain alike or similar result without departing from the spirit and scope ofthe invention.

Example 1 Exemplary Materials and Methods

Exemplary embodiments of materials and methods for use in the inventionare described in this Example.

Cell Culture

While autologous HDFs harvested from the patient are used to constructthe implant, preliminary studies are performed using neonatal foreskinfibroblasts, as there are convenient sources of cells for experimentalpurpose, for example. Further studies using autologous cells harvestedfrom the patient are performed to demonstrate that the procedure workswith these cells.

Neonatal foreskin HDFs are obtained from Cascade Biologics (Portland,Oreg.) and expanded in vitro with DMEM (Invitrogen, Carlsbad, Calif.,USA), containing 10% FBS (Invitrogen) and antibiotics. Suspensions ofHDFs are seeded in alginate or in monolayer culture as described below.

To generate alginate gel cultures, cells are suspended at high density(10⁷ cells/ml) in 2% wt/vol medium viscosity alginate (Sigma-Aldrich,St. Louis, Mo.), and 25 mL droplets are crosslinked in 100 mM CaCl₂,0.9% NaCl solution. The resulting alginate beads are then washedextensively in DMEM containing 10% FBS and antibiotics. Alginate beadsare immersed in DMEM containing 10% FBS and antibiotic supplemented with100 ng/ml recombinant human Bone Morphogenic Protein-2 (BMP-2) and 50 mgascorbic acid. Such conditions: high cell density and culture with BMP-2and ascorbic acid have been chosen because they are known to stimulatechondroinduction (Watt, 1988; Dozin et al., 1992; Sullivan et al., 1994;Denker et al., 1999; Zur Nieden et al., 2005; Zhou et al., 2004).

To generate monolayer cultures, HDFs are seeded in plastic flasks withan oxygen level of 20% in DMEM containing 10% FBS without BMP-2 andwithout ascorbic acid. These cells serve as control.

Culture Under 5% and 20% O₂

Cell-embedded alginate beads are kept under an atmosphere of 5% O₂, 5%CO₂, and 90% N₂ in an O₂-/CO₂-regulated incubator (low oxygen tension)or under 20% O₂, 5% CO₂, and 75% N₂ in an CO₂-regulated incubator(atmospheric oxygen tension) and cultured for 3 weeks. Then, assessmentof chondrogenic differentiation is performed (see Example 3, forexample).

Hydrostatic Compression

Cell-embedded alginate beads are divided into pressurized and controlgroups, and those from each group placed in separate flexiblepolyethylene/nylon bags permeable to oxygen and carbon dioxide. The bagsare filled with 15 ml of medium and are heat-sealed to exclude all air.

The bags in the pressurized group are placed within a newly developeddevice designed for the application of cyclic hydrostatic compression(Elder et al., 2005). This device allows the comparison of loadingregimes in a wide physiologic range under an equal three-dimensionalculture conditions. It consists of a large cylindrical stainless steelbase connected to a lid by bolts that compress an intervening o-ring. Ahydraulic cylinder is welded to the lid so that its interior iscontinuous with that of the chamber. The cylinder and chamber arecompletely filled with water, so that rapid hydrostatic compression isachieved by a force (generated by a MTS servohydraulic testing machine)applied to the cylinder's piston. A stable 37° C. is maintained byimmersing the chamber in a temperature-regulated circulating water bath.Bags in the control group are placed in a separate, water-filledstainless steel chamber in the same water bath.

The magnitude and frequency of the applied pressure are chosen to bewithin the physiological ranges (Mow et al., 1992) that have previouslybeen demonstrated to stimulate chondrogenic differentiation ofmultipotential mesenchymal cells (Elder et al., 2005) andredifferentiation of dedifferentiated chondrocytes (Domm et al., 2000).Short and long duration pressurization are tested and a successfulchondroinductive hydrostatic pressurization model is determined betweenthe short and long duration hydrostatic pressurization by quantitativeand qualitative assessment of chondrogenesis.

An exemplary regimen comprises the following:

1.0 Hz sinusoidal hydrostatic compression waveform with a minimumapplied pressure of 0.3 MPa and a maximum 5.0 MPa. For short durationpressurization, the cells are pressurized 1 h/day for 7 days. For longduration pressurization, the cells are pressurized 4 h/day for 7 days.Each day, immediately upon completion of loading, cultures are removedfrom the pressure vessel and returned to a water bath inside the tissueculture incubator.

Cell viability and chondrogenic differentiation of HDFs underhydrostatic cyclic compression and cultured under specific conditions(such as hypoxia, chondrogenic medium, high cell density) are assessedusing techniques standard in the art.

In another embodiment, the conversion of fibroblast cells intochondrocytes is induced by hydrostatic cyclic pressure and shear stress.In this case, the cells are seeded into a microfluidic scaffold.

Assessment of chondrogenic differentiation is performed (see Example 3,for example).

Example 2 Assessment of Cell Viability of HDFs in Alginate Beads

The viability of HDFs in alginate beads cultured in chondrogenic mediumis tested by light microscopy and/or viability test, in specific aspectsof the invention. Light microscopy is employed to study morphology andproliferation of HDFs. In an exemplary viability test, alginate beadsare dissolved in dissolving-buffer (0.55 M Na-Citrate, 1.5 M NaCl, and0.5 M EDTA), cells are centrifuged, and the pellet is treated withcollagenase for 1 h. Cells are resuspended in DMEM, and viability isdetermined using a Neubauer chamber and the trypan blue exclusionmethod, for example.

Example 3 Assessment of Chondrogenic Differentiation

In specific embodiments, HDFs are characterized by the production ofcollagen of type I, III and V, while chondrocytes are characterized bythe production of collagen of type II, IX, XI and the production ofsulfated proteoglycans.

Chondrogenic differentiation is assessed by measuring sulfatedglycosaminoglycan (sGAG) content and collagen I et II production bywestern blotting. The rate of collagen synthesis is measured by[³H]-proline incorporation.

Total DNA and sGAG Content

Cells in alginate beads are recovered from the alginate using 55 mMsodium citrate, 0.9% NaCl solution. Then the cells are lysed in 300 μlof 0.5% v/v Nonidet P-40 buffer (50 mM Tris-Cl, 100 mM NaCl, 5 mMMgCl₂). The lysate is transferred to microcentrifuge tubes, spun, andDNA is measured in a 100 μl supernatant aliquot using the Hoescht dyemethod (DNA Quantification Kit, Sigma, St. Louis, Mo.) with calf thymusDNA as standard. The remaining lysis buffer is removed and sGAG digestedin 100 μl of 2% v/v papain, 20 mM sodium acetate (pH 6) overnight at 60°C. Total sGAG content is then measured by the dimethylmethylene blueprecipitation method (Blyscan Glycoaminoglycan Assay, Biocolor, Ltd.)using chondroitin 4-sulfate purified from bovine trachea as standard.For each sample, the sGAG content is normalized to the DNA content.

Western Blot for Collagen Type I and Type II

Five beads of each sample are dissolved in 400 ml buffer (55 mM sodiumcitrate, 150 mM NaCl). For collagen solubilization, 100 μl of 0.25 Macetic acid and 100 pepsin solution (1 mg/ml 50 mM acetic acid: P-6887,Sigma) are added and the mixture kept at 4° C. for 24 h. Then, 100 μl ofa 10× stock solution TBS (1 M Tris, 2M NaCl and 50 mM CaCl₂, pH 8) and100 ml pancreatic elastase (1 mg/ml TBS; Sigma E-6883) are added andsamples incubated for 30 min at 37° C. The samples are centrifuged for10 min at 9000×g. The supernatant is collected. 25 μl of bovine collagentype I, bovine collagen type II (Sigma) or sample (each containing 5 mgtotal protein; quantification with Bio-Rad protein assay) are mixed with6 μl sample buffer, denatured for 5 min at 95° C., and loaded on a 7%acrylamide gel. Electrophoresis is performed. Gel is transferred ontothe blotting membrane. The membrane is blocked overnight inblocking-buffer (10% milk powder in TBST buffer) and then incubated witha mouse monoclonal antibody anti-collagen type I antibody (COL-1, ab6308, Abcam Inc) or a mouse monoclonal antibody anti-collagen type II(5B2.5, ab3092, Abcam Inc) overnight at 4° C. The membrane is washedwith TBST buffer. The goat antimouse biotin conjugated secondaryantibody is added (1:500) for 1 h followed by streptavidin-HRP at 1:1000dilution for 1 h. Blot is developed using ECL from Amersham.

Measure of [³H]-Proline Incorporation

In alginate beads in which the rate of collagen production isdetermined, the medium is removed and replaced with DMEM supplementedwith 10% FBS, antibiotics, 25 mg ascorbic acid, [³H] proline at 10μCi/ml, and 100 μg/ml β-amino-propionitrile (β-APN) to inhibit collagencross-link formation. After a 24 h incubation period, the incorporationof [³H] proline into collagen is measured. Beads are digested at 65° C.overnight in 1 ml papain solution [0.125 mg/ml (2.125 units/ml, Sigma),0.1 M Na₂HPO₄, 0.01 M EDTA, pH 6.5]. 200 ml of each sample are added to2 ml of scintillation fluid and measured using a scintillation counter.

500 μl of each sample is mixed with 500 μl PBS and used to determine theDNA content. Samples and blanks (containing 1 ml PBS) are treated withan ultrasonic beam for 15 s. 0.5 ml of RNAse and 0.5 ml pronase areadded and incubated at 37° C. for 30 min. Then, 0.5 ml of ethidiumbromide is added, samples are incubated for 30 min, and they aremeasured with a fluorometer.

[³H]-proline incorporation is normalized to total DNA content.

Example 4 Exemplary Design of Studies

In specific aspects of the invention, cell viability and chondrogenicdifferentiation of HDFs seeded are determined in three-dimensionalalginate bead cultures. In particular, cell viability and chondrogenicdifferentiation of HDFs seeded in alginate beads and cultured in achondrogenic medium (medium supplemented with BMP-2 and ascorbic acid)under 20% O₂ are compared to HDFs in monolayer cultures in DMEM with 10%FBS under 20% O₂ using the exemplary method described above.

In another aspect of the invention, the effects of oxygen tension on thedifferentiation of HDFs cultured in alginate beads is determined. HDFsseeded in alginate beads in the chondrogenic medium are cultured for 3weeks in 2 different oxygen tension: 1) low oxygen tension of 5% O₂, 5%CO₂, and 90% N₂ in an O₂-/CO₂-regulated incubator; and 2) atmosphericoxygen tension of 20% O₂, 5% CO₂, and 75% N₂ in an CO₂-regulatedincubator.

Chondrogenic differentiation is compared using the exemplary methoddescribed above.

In an additional embodiment of the invention, the effects of hydrostaticcompression on the differentiation of HDFs cultured in alginate beadsare determined. HDFs seeded in alginate beads in the chondrogenic mediumare subjected to different stimuli: 1) 1 h/day for 7 days hydrostaticpressure (1.0 Hz sinusoidal hydrostatic compression min 0.3 MPa max 5.0Mpa) and 20% O₂; 2) 4 h/day for 7 days hydrostatic pressure (1.0 Hzsinusoidal hydrostatic compression min 0.3 MPa max 5.0 Mpa) and 20% O₂;3) 1 h/day for 7 days hydrostatic pressure (1.0 Hz sinusoidalhydrostatic compression min 0.3 MPa max 5.0 Mpa) and 5% O₂; 4 h/day for7 days hydrostatic pressure (1.0 Hz sinusoidal hydrostatic compressionmin 0.3 MPa max 5.0 Mpa) and 5% O₂.

Chondrogenic differentiation may be assessed using the exemplary methoddescribed above.

REFERENCES

All patents and publications mentioned in the specification areindicative of the level of those skilled in the art to which theinvention pertains. All patents and publications are herein incorporatedby reference in their entirety to the same extent as if each individualpublication was specifically and individually indicated to beincorporated by reference.

Patents

U.S. Pat. No. 6,489,165

U.S. Pat. No. 6,627,422

Publications

Barry F, Boyton R E, Liu B et al. Chondrogenic differentiation ofmesenchymal stem cells from bone marrow: differentiation-dependent geneexpression of matrix components. Exp Cell Res 2001 (268):189-200.

Carter D R, Orr T E, Fyhrie D P, Schurman D J. Influences of mechanicalstress on prenatal and postnatal skeletal development. Clin Orthop1987(219):237-250.

Cui, L., Yin, S., Deng, C L., Yang, G H., Chen, F G., Liu, W., Liu, DL., Cao, Y L. Cartilage-derived morphogenetic protein 1 initiateschondrogenic differentiation of human dermal fibroblasts in vitro.Zhonghua Yi Xue Za Zhi. 2004 Aug. 2; 84(15):1304-1309.

Denker A E, Haas A R, Nicoll S B, Tuan R S. Chondrogenic differentiationof murine C3H10T1/2 multipotential mesenchymal cells: I. Stimulation bybone morphogenic protein-2 in high-density micromass culturesDifferentiation 1999; 64:67-76

Domm C, Fay J, Schunke M, Kurz B. Redifferentiation of dedifferentiatedjoint cartilage cells in alginate culture. Effect of intermittenthydrostatic pressure and low oxygen partial pressure Orthopade 2000February; 29(2):91-99

Dozin, R. Quarto, G. Campanile & R. Cancedda: In vitro differentiationof mouse embryo chondrocytes: requirement for ascorbic acid. Eur J CellBiol 1992; 58, 390-4

Elder S H, Fulzele K S, McCulley W R. Cyclic hydrostatic compressionstimulates chondroinduction of C3H/10T1/2 cells. Biomechan ModelMechanobiol 2005(3): 141-146

French M M, Rose S, Canseco J and Athanasiou K A. Chondrogenicdifferentiation of adult dermal fibroblasts. Annals of BiomedicalEngineering 2004; 32 (1):50-56.

Hauselmann H J, Aydelotte M B, Schumacher B L, Kuettner K E, Gitelis SH, Thonar E J. Synthesis and turnover of proteoglycans by human andbovine adult articular chondrocytes cultured in alginate beads. Matrix1992(12):116-129.

Kessler, D., Dethlefsen, S., Haase, I., Plomann, M., Hirche, F., Krieg,T., Eckes, B. Fibroblasts in mechanically stressed collagen latticesassume a “synthetic” phenotype. J. Biol. Chem. 2001 September;276(39):36575-36585.

Majumdar M K, Wang E and Morris E A. BMP-2 and BMP-9 promoteschondrogenic differentiation of human multipotential mesenchymal cellsand overcomes the inhibitory effect of IL-1. J. Cell. Physiol.2001(189):275-284.

Meisel, H J., Alasevic, O., Hutton, W., Ganey, T. Disc repair withautologous chondrocytes: A pilot clinical study. European Cells andMaterials. Vol. 10 Suppl. 3, 2005 (page 39) Watt F M. Effect of seedingdensity on stability of the dedifferentiated phenotype of pig articularchondrocytes in culture. J Cell Sci 1988; 89:373-378.

Mizuno H, Roy A K, Vacanti C A, Kojima K, Ueda M, and Bonassar L J.Tissue-engineered composites of annulus fibrosus and nucleus pulposusfor intervertebral disc replacement. Spine 2004 (29):1290-1298.

Mow V C, Ratcliffe A, Poole A R. Cartilage and diarthrodial joints asparadigms for hierarchical materials and structures. Biomaterials 1992;13(2):67-97.

Nicoll S B., Wedrychowska, A., Smith, N R., Bhatnagar, R S. Modulationof proteoglycan and collagen profiles in human dermal fibroblasts byhigh density micromass culture and treatment with lactic acid suggestschange to a chondrogenic phenotype. Connect. Tissue Res. 2001;42(1):59-69.

T. A. Sullivan, B. Uschmann, R. Hough & P. S. Leboy: Ascorbatemodulation of chondrocyte gene expression is independent of its role incollagen secretion. J Biol Chem 1994; 36, 22500-6

Watt F M. Effect of seeding density on stability of the dedifferentiatedphenotype of pig articular chondrocytes in culture. J Cell Sci 1988;89:373-378

Zhou S, Glowacki J, and Yates K E. Comparison of TGF-b/BMP pathwayssignaled by demineralized bone powder and BMP-2 in human dermalfibroblasts. J Bone Miner Res 2004; 19:1732-1741.

Zur Nieden N I, Kempka G, Rancourt D E, Ahr H J. Induction of chondro-,osteo- and adipogenesis in embryonic stem cells by bone morphogenicprotein-2: effect ofcofactors on differentiating lineages. BMC Dev Biol,2005; Jan. 26 (5):1-15

Although the present invention and its advantages have been described indetail, it should be understood that various changes, substitutions andalterations can be made herein without departing from the spirit andscope of the invention as defined by the appended claims. Moreover, thescope of the present application is not intended to be limited to theparticular embodiments of the process, machine, manufacture, compositionof matter, means, methods and steps described in the specification. Asone of ordinary skill in the art will readily appreciate from thedisclosure of the present invention, processes, machines, manufacture,compositions of matter, means, methods, or steps, presently existing orlater to be developed that perform substantially the same function orachieve substantially the same result as the corresponding embodimentsdescribed herein may be utilized according to the present invention.Accordingly, the appended claims are intended to include within theirscope such processes, machines, manufacture, compositions of matter,means, methods, or steps.

1.-58. (canceled)
 59. A hybrid structure for cartilage repair,comprising: an encapsulating device comprising inert material; and aliving core comprising chondrocyte-like cells, wherein saidencapsulating device encapsulates the living core. 60.-61. (canceled)